Nematic liquid crystal composition and liquid crystal display device

ABSTRACT

There is provided a liquid crystal composition having a sufficiently low viscosity (η), a sufficiently low rotational viscosity (γ1), a high elastic constant (K 33 ), and negative Δ∈ with a high absolute value without decreasing the refractive index anisotropy (Δn) and the nematic phase-isotropic liquid phase transition temperature (T ni ); and a liquid crystal display device with a VA mode or the like that uses the liquid crystal composition and has high display quality and high response speed. The liquid crystal display device that uses the liquid crystal composition of the present invention has a distinguished feature of high-speed response and is particularly useful as an active matrix driving liquid crystal display device. The liquid crystal display device is applicable to a VA mode, PSVA mode, PSA mode, IPS mode, or ECB mode liquid crystal display device.

TECHNICAL FIELD

The present invention relates to a nematic liquid crystal composition which has a negative dielectric anisotropy (Δ∈) and is useful as a liquid crystal display material, and to a liquid crystal display device using the nematic liquid crystal composition.

BACKGROUND ART

Liquid crystal display devices have been used for clocks, calculators, household electric appliances, measuring instruments, panels for automobiles, word processors, electronic organizers, printers, computers, televisions, etc. Typical examples of a liquid crystal display mode include a TN (twisted nematic) mode, an STN (super twisted nematic) mode, a DS (dynamic scattering) mode, a GH (guest-host) mode, an IPS (in-plane switching) mode, an OCB (optically compensated birefringence) mode, an ECB (electrically controlled birefringence) mode, a VA (vertical alignment) mode, a CSH (color super-homeotropic) mode, and FLC (ferroelectric liquid crystal). Examples of a driving method include static driving, multiplex driving, passive matrix driving, and active matrix (AM) driving performed using TFTs (thin film transistors), TFDs (thin film diodes), and the like.

In an IPS mode, an ECB mode, a VA mode, a CSH mode, or the like among these display modes, a liquid crystal composition having negative Δ∈ is used. In particular, a VA mode by AM driving is used for display devices required to have high-speed response and a wide viewing angle, such as televisions.

A liquid crystal composition containing the following liquid crystal compounds (A) and (B) having a 2,3-difluorophenylene skeleton (refer to PTL 1) has been disclosed as a liquid crystal composition having negative Δ∈.

This liquid crystal composition contains liquid crystal compounds (C) and (D) as liquid crystal compounds whose Δ∈ is substantially zero. However, a sufficiently low viscosity has not been achieved in liquid crystal compositions required to have high-speed response for liquid crystal televisions or the like.

A liquid crystal composition containing a liquid crystal compound (E) has been disclosed. There have been proposed a liquid crystal composition containing the liquid crystal compound (E) together with the liquid crystal compound (D) to achieve a low refractive index anisotropy Δn (refer to PTL 2) and a liquid crystal composition to which a liquid crystal compound (F) is added to improve the response speed (refer to PTL 3).

A liquid crystal composition containing a liquid crystal compound (G) and the liquid crystal compound (F) has also been disclosed (refer to PTL 4). However, a higher response speed has been required.

A liquid crystal composition containing the liquid crystal compound (A), the liquid crystal compound (G), and a liquid crystal compound whose Δ∈ is substantially zero and which is represented by formula (I) in a combined manner has been disclosed (refer to PTL 5). In the production process of liquid crystal display devices, however, an extremely low pressure is required when a liquid crystal composition is injected into a liquid crystal cell. Therefore, a compound having low vapor pressure is volatilized and thus it is believed that the content of such a compound cannot be increased. Consequently, in the liquid crystal composition, the content of the liquid crystal compound represented by the formula (I) is limited, and thus the liquid crystal composition exhibits high Δn, but unfavorably has a considerably high viscosity.

Furthermore, a liquid crystal composition containing a compound having a terphenyl structure subjected to substitution with fluorine has also been disclosed in PTL 6 and PTL 7.

It has been disclosed in PTL 8 that the response speed of a homeotropic liquid crystal cell is improved by using a liquid crystal material having a large index represented by (formula 1), but the improvement is not sufficient. [Math. 1] FoM=K ₃₃ ·Δn ²/γ1  (Formula 1)

-   -   K₃₃: elastic constant     -   Δn: refractive index anisotropy     -   γ1: rotational viscosity

In liquid crystal compositions required to have high-speed response for liquid crystal televisions or the like, the following has been required: the refractive index anisotropy (Δn) and the nematic phase-isotropic liquid phase transition temperature (T_(ni)) are not decreased, the viscosity (η) is sufficiently decreased, the rotational viscosity (γ1) is sufficiently decreased, and the elastic constant (K₃₃) is increased.

CITATION LIST Patent Literature

PTL 1: Japanese Unexamined Patent Application Publication No. 8-104869

PTL 2: European Patent Application Publication No. 0474062

PTL 3: Japanese Unexamined Patent Application Publication No. 2006-037054

PTL 4: Japanese Unexamined Patent Application Publication No. 2001-354967

PTL 5: WO2007/077872

PTL 6: Japanese Unexamined Patent Application Publication No. 2003-327965

PTL 7: WO2007/077872

PTL 8: Japanese Unexamined Patent Application Publication No. 2006-301643

SUMMARY OF INVENTION Technical Problem

It is an object of the present invention to provide a liquid crystal composition having a sufficiently low viscosity (η), a sufficiently low rotational viscosity (γ1), a high elastic constant (K₃₃), and a negative dielectric anisotropy (Δ∈) with a high absolute value without decreasing the refractive index anisotropy (Δn) and the nematic phase-isotropic liquid phase transition temperature (T_(ni)), and to provide a liquid crystal display device with a VA mode or the like that uses the liquid crystal composition and has high display quality and high response speed.

Solution to Problem

The present inventors have conducted studies on various fluorobenzene derivatives and have found that the above object can be achieved by combining particular compounds. Thus, the present invention has been completed.

The present invention provides a liquid crystal composition containing one or more fluorobenzene derivatives having a 1-propenyl group as a first component and one or more liquid crystal compounds having negative Δ∈ with an absolute value of 3 or more as a second component. The present invention also provides a liquid crystal display device that uses the liquid crystal composition.

Advantageous Effects of Invention

The liquid crystal composition of the present invention is a liquid crystal composition having a sufficiently low viscosity (η), a sufficiently low rotational viscosity (γ1), and a high elastic constant (K₃₃) without decreasing the refractive index anisotropy (Δn) and the nematic phase-isotropic liquid phase transition temperature (T_(ni)), and a liquid crystal display device with a VA mode or the like that has high display quality and high response speed can be provided by using the liquid crystal composition.

DESCRIPTION OF EMBODIMENTS

The liquid crystal composition of the present invention contains one or more fluorobenzene derivatives having a 1-propenyl group as a first component, and preferably contains 1 to 15 of the fluorobenzene derivatives and more preferably contains 2 to 10 of the fluorobenzene derivatives.

The fluorobenzene derivative having a 1-propenyl group is specifically a compound in which a mesogenic skeleton having a 2,3-difluoro phenyl group has a 1-propenyl group as a terminal group, and preferably a compound represented by general formula (I).

In the formula, R¹¹ represents an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkenyl group having 2 to 8 carbon atoms, or an alkenyloxy group having 2 to 8 carbon atoms. R¹¹ preferably represents an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms. Z¹¹ and Z¹² each independently represent —OCH₂—, —CH₂O—, —CF₂O—, —OCF₂—, —CH₂CH₂—, —CF₂CF₂—, or a single bond, preferably each independently represent —CH₂O—, —CF₂O—, or a single bond, and more preferably each independently represent —CH₂O— or a single bond. Ring A and Ring B each independently represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, a 2-fluoro-1,4-phenylene group, a 3-fluoro-1,4-phenylene group, a 3,5-difluoro-1,4-phenylene group, a 2,3-difluoro-1,4-phenylene group, a 1,4-cyclohexenylene group, a 1,4-bicyclo[2.2.2]octylene group, a piperidine-1,4-diyl group, a naphthalene-2,6-diyl group, a decahydronaphthalene-2,6-diyl group, or a 1,2,3,4-tetrahydronaphthalene-2,6-diyl group. Ring A and Ring B preferably each independently represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, a 2-fluoro-1,4-phenylene group, a 3-fluoro-1,4-phenylene group, a 3,5-difluoro-1,4-phenylene group, or a 2,3-difluoro-1,4-phenylene group and more preferably each independently represent a trans-1,4-cyclohexylene group or a 1,4-phenylene group. Furthermore, m and n each independently represent 0, 1, or 2 and preferably each independently represent 0 or 1, and m+n preferably represents 1 or 2.

The content of the compounds represented by the general formula (I) is 3 mass % to 70 mass %, preferably 5 mass % to 50 mass %, and more preferably 10 mass % to 40 mass %.

The compounds represented by the general formula (I) are, for example, preferably represented by general formula (I-A1), (I-B1), (I-C1), (I-D1), (I-E1), (I-A2), (I-B2), (I-C2), (I-D2), or (I-E2).

In the formulae, R¹¹ represents the same as above.

The liquid crystal composition of the present invention contains one or more liquid crystal compounds having a negative dielectric anisotropy (Δ∈) with an absolute value of 3 or more as a second component, preferably contains liquid crystal compounds having a negative dielectric anisotropy (Δ∈) with an absolute value of 4 or more, and more preferably contains liquid crystal compounds having a negative dielectric anisotropy (Δ∈) with an absolute value of 5 or more. The dielectric anisotropy (Δ∈) of a liquid crystal compound is determined by extrapolating the measurement value of dielectric anisotropy (Δ∈) of a composition prepared by adding 10 mass % of the liquid crystal compound to a liquid crystal composition whose dielectric anisotropy at 25° C. is about 0.

The second component preferably includes a compound selected from the group of compounds represented by general formula (II-A) and or general formula (II-B).

In the formulae, R¹ and R² each independently represent an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkenyl group having 2 to 8 carbon atoms, or an alkenyloxy group having 2 to 8 carbon atoms; one —CH₂— or two or more non-adjacent —CH₂— in R¹ and R² may be each independently substituted with —O— and or —S—; one or more hydrogen atoms in R¹ and R² may be each independently substituted with a fluorine atom or a chlorine atom; and R¹ and R² do not represent a 1-propenyl group. R¹ and R² in the formulae preferably each independently represent a linear alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms. More specifically, R¹ more preferably represents an alkenyl group having 2 to 5 carbon atoms to increase the elastic constant K₃₃.

Ring A and Ring B each independently represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, a 2-fluoro-1,4-phenylene group, a 3-fluoro-1,4-phenylene group, a 3,5-difluoro-1,4-phenylene group, a 2,3-difluoro-1,4-phenylene group, a 1,4-cyclohexenylene group, a 1,4-bicyclo[2.2.2]octylene group, a piperidine-1,4-diyl group, a naphthalene-2,6-diyl group, a decahydronaphthalene-2,6-diyl group, or a 1,2,3,4-tetrahydronaphthalene-2,6-diyl group. Ring A and Ring B preferably each independently represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, a 2-fluoro-1,4-phenylene group, a 3-fluoro-1,4-phenylene group, a 3,5-difluoro-1,4-phenylene group, or a 2,3-difluoro-1,4-phenylene group and more preferably each independently represent a trans-1,4-cyclohexylene group or a 1,4-phenylene group.

Furthermore, p and q each independently represent 0, 1, or 2 and preferably each independently represent 0 or 1.

More specifically, the general formula (II-A) preferably includes general formulae (II-A1) to (II-A5) and the general formula (II-B) preferably includes general formulae (II-B1) to (II-B5).

In the formulae, R³ and R⁴ each independently represent an alkyl group having 1 to 8 carbon atoms or an alkenyl group having 2 to 8 carbon atoms; one or more hydrogen atoms in R³ and R⁴ may be each independently substituted with a fluorine atom; and R³ and R⁴ do not represent a 1-propenyl group. R³ and R⁴ in the formulae preferably each independently represent a linear alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms. More specifically, one of R³ and R⁴ more preferably represents an alkenyl group having 2 to 5 carbon atoms to increase the elastic constant K₃₃.

The liquid crystal composition of the present invention contains one or more of the second components, preferably contains 1 to 15 of the second components, and more preferably 2 to 10 of the second components.

The content of the second component is 3 mass % to 70 mass %, preferably 5 mass % to 50 mass %, and more preferably 10 mass % to 40 mass %.

The liquid crystal composition of the present invention may further contain one or more compounds selected from the group of compound represented by general formula (III-A) to general formula (III-J) as a third component, and preferably contains 1 to 10 compounds selected from the general formulae (III-A), (III-D), (III-F), (III-G), and (III-H).

In the formulae, R⁵ represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and R⁶ represents an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms. In the compound represented by the general formula (III-A), R⁵ preferably represents an alkenyl group having 2 to 5 carbon atoms, and R⁶ preferably represents an alkyl group having 1 to 5 carbon atoms.

One or more compounds represented by general formula (V) may be contained as an additional component.

In the formula, R²¹ and R²² each independently represent an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkenyl group having 2 to 8 carbon atoms, or an alkenyloxy group having 2 to 8 carbon atoms. R²¹ and R²² preferably each independently represent an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms.

The liquid crystal composition of the present invention preferably contains the compounds represented by the general formula (I), the general formula (II-A1), and the general formula (II-A2) at the same time, more preferably contains the compounds represented by the general formula (I), the general formula (II-A1), the general formula (II-A2), and the general formula(III-A) at the same time, and further preferably contains the compounds represented by the general formula (I), the general formula (II-A1), the general formula (II-A2), the general formula (III-A), and the general formula (V) at the same time.

The liquid crystal composition of the present invention preferably contains the compounds represented by the general formula (I), the general formula (II-B1), and the general formula (III-A) at the same time and more preferably contains the compounds represented by the general formula (I), the general formula (II-B1), the general formula (III-A), and the general formula (V) at the same time.

The liquid crystal composition of the present invention preferably contains the compounds represented by the general formula (I), the general formula (II-A), and the general formula (II-B) at the same time. Specifically, the liquid crystal composition preferably contains the compounds represented by the general formula (I), the general formula (II-A1), the general formula (II-A2), and the general formula (II-B1) at the same time and more preferably contains the compounds represented by the general formula (I), the general formula (II-A1), the general formula (II-A2), the general formula (II-B1), the general formula (III-A), and the general formula (V) at the same time.

In the liquid crystal composition of the present invention, the dielectric anisotropy (Δ∈) at 25° C. is −2.0 to −8.0, preferably −2.0 to −6.0, more preferably −2.0 to −5.0, and particularly preferably −2.5 to −4.0.

In the liquid crystal composition of the present invention, the refractive index anisotropy (Δn) at 20° C. is 0.08 to 0.14, preferably 0.09 to 0.13, and more preferably 0.09 to 0.12. More specifically, Δn is preferably 0.10 to 0.13 when a small cell gap is employed and 0.08 to 0.10 when a large cell gap is employed.

In the liquid crystal composition of the present invention, the viscosity (II) at 20° C. is 10 to 30 mPa·s, preferably 10 to 25 mPa·s, and more preferably 10 to 22 mPa·s.

In the liquid crystal composition of the present invention, the rotational viscosity (γ1) at 20° C. is 60 to 130 mPa·s, preferably 60 to 110 mPa·s, and more preferably 60 to 100 mPa·s.

In the liquid crystal composition of the present invention, the nematic phase-isotropic liquid phase transition temperature (T_(ni)) is 60° C. to 120° C., preferably 70° C. to 100° C., and more preferably 70° C. to 85° C.

In addition to the above compounds, the liquid crystal composition of the present invention may contain typical nematic liquid crystal, smectic liquid crystal, cholesteric liquid crystal, an antioxidant, an ultraviolet absorber, a polymerizable monomer, and the like.

For example, a polymerizable compound such as a biphenyl derivative or a terphenyl derivative is contained as a polymerizable monomer, and the content of the polymerizable compound is preferably 0.01% to 2%.

More specifically, the liquid crystal composition of the present invention preferably contains one or more polymerizable compounds represented by general formula (IV).

In the formula, R⁷ and R⁸ each independently represent any of groups represented by formula (R-1) to formula (R-15) below.

X¹ to X⁸ each independently represent a trifluoromethyl group, a trifluoromethoxy group, a fluorine atom, or a hydrogen atom.

The biphenyl skeleton in the general formula (IV) is preferably selected from biphenyl skeletons represented by formula (IV-11) to formula (IV-14) and is more preferably a biphenyl skeleton represented by formula (IV-11).

Polymerizable compounds having the skeletons represented by the formula (IV-11) to the formula (IV-14) exhibit an optimum anchoring strength after being polymerized, and thus a good alignment state is achieved.

A polymerizable compound-containing liquid crystal composition that contains the first component, the second component, the third component, and the polymerizable compound represented by the general formula (IV) in the present invention at the same time has a low viscosity (η), a low rotational viscosity (γ1), and a high elastic constant (K₃₃). Therefore, a PSA mode or PSVA mode liquid crystal display device that uses such a polymerizable compound-containing liquid crystal composition can achieve high-speed response.

A liquid crystal display device that uses the liquid crystal composition of the present invention has a distinguished feature of high-speed response and is particularly useful as an active matrix driving liquid crystal display device. The liquid crystal display device is applicable to a VA mode, PSVA mode, PSA mode, IPS mode, or ECB mode liquid crystal display device.

EXAMPLES

The present invention will now be further described in detail on the basis of Examples, but the present invention is not limited to Examples. In compositions of Examples and Comparative Examples below, “%” means “mass %”. In Examples, the following abbreviations are used for the description of compounds.

(Side chain) -n —C_(n)H_(2n+1) linear alkyl group having n carbon atoms n- C_(n)H_(2n+1)— linear alkyl group having n carbon atoms —On —OC_(n)H_(2n+1) linear alkoxy group having n carbon atoms nO— C_(n)H_(2n+1)O— linear alkoxy group having n carbon atoms —V —CH═CH₂ V— CH₂═CH— —V1 —CH═CH—CH₃ 1-propenyl group 1V— CH₃—CH═CH— 1-propenyl group -2V —CH₂—CH₂—CH═CH₃ V2- CH₃═CH—CH₂—CH₂— -2V1 —CH₂—CH₂—CH═CH—CH₃ 1V2- CH₃—CH═CH—CH₂—CH₂ (Linking group) -nO— —C_(n)H_(2n)O— (Ring structure)

In Examples, the measured properties are as follows.

T_(ni): nematic phase-isotropic liquid phase transition temperature (° C.)

Δn: refractive index anisotropy at 20° C.

Δ∈: dielectric anisotropy at 25° C.

η: viscosity (mPa·s) at 20° C.

γ1: rotational viscosity (mPa·s) at 20° C.

K₃₃: elastic constant K₃₃ (pN) at 20° C.

Comparative Examples 1 and 2 and Examples 1, 2, and 3

LC-A (Comparative Example 1), LC-B (Comparative Example 2), LC-1 (Example 1), LC-2 (Example 2), and LC-3 (Example 3) each having a composition listed in Table 1 were prepared, and the physical properties were measured. The results are as follows.

TABLE 1 Comparative Comparative Example Example Example Example 1 Example 2 1 2 3 LC-A LC-B LC-1 LC-2 LC-3 1V-Cy-1O—Ph5—O2 General — — 11 12 12 formula (I) 1V-Cy-Cy-1O—Ph5—O2 General — — 13 12 12 formula (I) 2-Cy-1O—Ph5—O2 General 3 3 — — — formula (II-A) 3-Cy-1O—Ph5—O2 General 6 5 — — 2 formula (II-A) 2-Cy—Cy-1O—Ph5—O2 General 10 7 13 4 4 formula (II-A) 3-Cy—Cy-1O—Ph5—O2 General 10 7 — 4 4 formula (II-A) 4-Cy—Cy-1O—Ph5—O2 General 10 7 — — formula (II-A) V-Cy—Cy-1O—Ph5—O2 General — 10 — 5 — formula (II-A) 3-Cy—Ph—Ph5—O2 General — — — 4 formula (II-B) 3-Cy—Cy—V General 38 38 38 42 39 formula (III-A) 3-Cy—Cy—V1 General — — 4 — 3 formula (III-A) 3-Ph—Ph-1 General 3 3 3 1.5 3 formula (III-F) 5-Ph—Ph-1 General 2 2 — 1.5 — formula (III-F) 3-Ph—Ph5—Ph-1 General 9 9 9 4 — formula (V) 3-Ph—Ph5—Ph-2 General 9 9 9 4 — formula (V) V2-Ph—Ph5—Ph-2V General — — — 10 12 formula (V) 1V2-Ph—Ph5—Ph-2V1 General — — — — 5 formula (V) Total 100 100 100 100 100 Tni [° C.] 76.1 76.3 76.0 76.2 76.4 Δn 0.108 0.109 0.108 0.108 0.109 η [mPa · s] 14.6 14.5 14.1 13.7 13.9 γ1 [mPa · s] 98 99 99 96 95 Δε −3.2 −3.1 −3.2 −3.1 −3.2 K₃₃ [pN] 13.9 14.2 16.0 15.8 16.1 γ1/K₃₃ 7.1 7.0 6.2 6.1 5.9

The liquid crystal compositions LC-1, LC-2, and LC-3 of the present invention had a low viscosity (11), a low rotational viscosity (γ1), and a considerably high elastic constant (K₃₃). Therefore, γ1/K₃₃ of LC-1, LC-2, and LC-3 were 6.2, 6.1, and 5.9, respectively, which were much lower than those of LC-A and LC-B of Comparative Examples. The response speed of each of liquid crystal display devices including the liquid crystal compositions was measured. The liquid crystal display devices including LC-1, LC-2, and LC-3 had a sufficiently high response speed, which was higher than the response speed of LC-A and LC-B by 10% or more. Furthermore, the voltage holding ratio (VHR) was measured, and it was confirmed that high VHR was achieved. The cell thickness was 3.5 μm and the alignment film was JALS2096. The response speed was measured at 20° C. using DMS301 manufactured by AUTRONIC-MELCHERS with Von of 5.5 V and Voff of 1.0 V. The VHR was measured using VHR-1 manufactured by TOYO Corporation at a voltage of 5 V at a frequency of 60 Hz at a temperature of 60° C. Although the conditions of injection into liquid crystal cells (pressure and the ODF method) were changed, the physical properties did not change.

Comparative Example 3 and Example 4

LC-C (Comparative Example 3) and LC-4 (Example 4) each having a composition listed in Table 2 were prepared, and the physical properties were measured. The results are as follows.

TABLE 2 Comparative Example 3 Example 4 LC-C LC-4 1V-Cy—Ph5-2 General — 4 formula (I) 1V-Cy-1O—Ph5—O2 General — 7 formula (I) 1V-Cy—Cy—Ph5-1 General — 4 formula (I) 1V-Cy—Cy-1O—Ph5—O2 General — 7 formula (I) 3-Cy-1O—Ph5—O1 General 5 — formula (II-A) 3-Cy—Cy-1O—Ph5—O2 General 10 3 formula (II-A) V-Cy—Cy-1O—Ph5—O2 General 10 8 formula (II-A) 3-Cy—Ph5-2 General 4 — formula (II-B) 3-Cy—Cy—Ph5-1 General 4 — formula (II-B) 3-Cy—Cy—V General 37 37 formula (III-A) 3-Cy—Cy-2 General — 3 formula (III-A) 5-Ph—Ph-1 General 8 5 formula (III-F) 3-Ph—Ph5—Ph-1 General 8 8 formula (V) 3-Ph—Ph5—Ph-2 General 11 11 formula (V) 3-Ph—Ph5—Ph-3 General 3 3 formula (V) Total 100 100 Tni [° C.] 72.3 73.1 Δn 0.114 0.114 η [mPa · s] 13.9 13.5 γ1 [mPa · s] 90 88 Δε −2.7 −2.7 K₃₃ [pN] 13.2 14.4 γ1/K₃₃ 6.8 6.1

The liquid crystal composition LC-4 of the present invention had a low viscosity (η), a low rotational viscosity (γ1), and a high elastic constant (K₃₃). Therefore, γ1/K₃₃ of LC-4 was 6.1, which was much lower than that of LC-C of Comparative Example. The response speed of each of liquid crystal display devices including the liquid crystal compositions was measured. The liquid crystal display device including LC-4 had a higher response speed than the liquid crystal display device including LC-C. Furthermore, the voltage holding ratio (VHR) was measured, and it was confirmed that high VHR was achieved. The cell thickness was 3.5 μm and the alignment film was JALS2096. The response speed was measured at 20° C. using DMS301 manufactured by AUTRONIC-MELCHERS with Von of 5.5 V and Voff of 1.0 V. The VHR was measured using VHR-1 manufactured by TOYO Corporation at a voltage of 5 V at a frequency of 60 Hz at a temperature of 60° C. Although the conditions of injection into liquid crystal cells (pressure and the ODF method) were changed, the physical properties did not change.

Comparative Example 4 and Example 5

LC-D (Comparative Example 4) and LC-5 (Example 5) each having a composition listed in Table 3 were prepared, and the physical properties were measured. The results are as follows.

TABLE 3 Comparative Example 4 Example 5 LC-D LC-5 1V-Cy—Ph5-2 General — 7 formula (I) 1V-Cy—Cy—Ph5-1 General — 7 formula (I) 3-Cy—Ph5—O2 General 12 5 formula (II-B) 3-Ph—Ph5—O2 General 10 10 formula (II-B) 3-Cy—Cy—Ph5—O2 General 11 4 formula (II-B) 2-Cy—Ph—Ph5—O2 General 7 7 formula (II-B) 3-Cy—Ph—Ph5—O4 General 7 7 formula (II-B) 4-Cy—Ph—Ph5—O3 General 6 6 formula (II-B) 3-Cy—Cy-2 General 19 23 formula (III-A) 3-Cy—Cy-4 General 6 4 formula (III-A) 3-Cy—Cy-5 General 6 4 formula (III-A) 3-Cy—Cy—V1 General 10 10 formula (III-A) 3-Cy—Cy—Ph-1 General 6 6 formula (III-G) Total 100 100 Tni [° C.] 76.3 76.5 Δn 0.093 0.095 η [mPa · s] 16.7 16.8 γ1 [mPa · s] 101 99 Δε −2.8 −2.8 K₃₃ [pN] 13.5 14.4 γ1/K₃₃ 7.5 6.7

The liquid crystal composition LC-5 of the present invention had a low viscosity (η), a low rotational viscosity (γ1), and a high elastic constant (K₃₃). Therefore, γ1/K₃₃ of LC-5 was 6.7, which was much lower than that of LC-D of Comparative Example. The response speed of each of liquid crystal display devices including the liquid crystal compositions was measured. The liquid crystal display device including LC-5 had a higher response speed than the liquid crystal display device including LC-D. Furthermore, the voltage holding ratio (VHR) was measured, and it was confirmed that high VHR was achieved. The cell thickness was 3.5 μm and the alignment film was JALS2096. The response speed was measured at 20° C. using DMS301 manufactured by AUTRONIC-MELCHERS with Von of 5.5 V and Voff of 1.0 V. The VHR was measured using VHR-1 manufactured by TOYO Corporation at a voltage of 5 V at a frequency of 60 Hz at a temperature of 60° C. Although the conditions of injection into liquid crystal cells (pressure and the ODF method) were changed, the physical properties did not change. It was confirmed from the above results that the liquid crystal composition of the present invention had sufficiently low a sufficiently low rotational viscosity γ1, a high elastic constant K₃₃, and a negative dielectric anisotropy (Δ∈) with a high absolute value without decreasing Δn and T_(ni), and a VA mode liquid crystal display device that uses the liquid crystal composition had high display quality and high response speed. 

The invention claimed is:
 1. A liquid crystal composition comprising: a first component comprising one or more fluorobenzene derivatives having a 1-propenyl group represented by general formula (I-1), and one or more fluorobenzene derivatives having a 1-propenyl group represented by general formula (I-2); and one or more liquid crystal compounds having negative Δ∈ with an absolute value of 3 or more as a second component,

in the general formula (I-2), R¹¹ represents an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms; Z¹¹ and Z¹² each represent —CH₂O—,—or a single bond; Ring A and Ring B each represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, or a 1,4-cyclohexenylene group; and m and n each independently represent 0 or 1,

in the general formula (I-2). R¹¹ represents an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms; Z¹¹ represents a single bond and Z¹² represents —CH₂O—, —CF₂O—, —CH₂CH₂—, or a single bond; Ring A and Ring B each independently represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, or a 1,4-cyclohexenylene group; and m represents 1 and n represents 1, wherein the one or more fluorobenzene derivatives having a 1-propenyl group represented by general formula (I-1) includes a compound wherein m represenis 0 and n represents
 1. 2. The liquid crystal composition according to claim 1, wherein the second component includes one or more compounds selected from the group of compounds represented by general formula (II-A) and/or general formula (II-B),

in the formulae, R^(i) and R² each independently represent an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkenyl group having 2 to 8 carbon atoms, or an alkenyloxy group having 2 to 8 carbon atoms; one -CH₂- or two or more non-adjacent - CH₂- in R^(l) and R² may be each independently substituted with -0- and or -S-; one or more hydrogen atoms in R^(l) and R² may be each independently substituted with a fluorine atom or a chlorine atom; R^(l) and R² do not represent a 1-propenyl group; Ring A and Ring B each independently represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, a 2-fluoro-1,4- phenylene group, a 3-fluoro-1,4-phenylene group, a 3,5-difluoro-1,4-phenylene group, a 2,3- difluoro-1,4-phenylene group, a 1,4-cyclohexenylene group, a 1,4-bicyclooctylene group, a piperidine-1,4-diyl group, a naphthalene-2,6-diyl group, a decahydronaphthalene-2,6-diyl group, or a 1,2,3,4-tetrahydronaphthalene-2,6-diyl group; and p and q each independently represent 0, 1, or
 2. 3. The liquid crystal composition according to claim 1, wherein a content of the first component is 3 mass % to 70 mass %.
 4. The liquid crystal composition according to claim 1, wherein a content of the second component is 3 mass % to 70 mass %.
 5. The liquid crystal composition according to claim 2, wherein the compounds represented by the general formula (II-A) are compounds represented by general formulae (II-A1) to (II-A5) and the compounds represented by the general formula (II-B) are compounds represented by general formulae (II-B1) to (II-B5),

in the formulae, R³ and R⁴ each independently represent an alkyl group having 1 to 8 carbon atoms or an alkenyl group having 2 to 8 carbon atoms; one or more hydrogen atoms in R³ and R⁴ may be each independently substituted with a fluorine atom; and R³ and R⁴ do not represent a 1-propenyl group.
 6. The liquid crystal composition according to claim 1, comprising, as a third component, one or more compounds selected from the group of compounds represented by general formulae (III-A) to (III-J),

in the formulae, le represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and R⁶ represents an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms.
 7. The liquid crystal composition according to claim 1, comprising, as an additional component, one or more compounds represented by general formula (V),

in the formula, R²¹ and R²² each independently represent an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkenyl group having 2 to 8 carbon atoms, or an alkenyloxy group having 2 to 8 carbon atoms.
 8. The liquid crystal composition according to claim 7, wherein the compounds represented by the general formula (I-1), the general formula (II-A), the general formula (III-A), and the general formula (V) are contained at the same time,

in the formulae, R⁵ represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and R⁶ represents an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms.
 9. The liquid crystal composition according to claim 7, wherein the compounds represented by the general formula (I-1), the general formula (II-B), the general formula (III-A), and the general formula (V) are contained at the same time,

in the formulae, R⁵ represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and R⁶ represents an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms.
 10. The liquid crystal composition according to claim 7, wherein the compounds represented by the general formula (I-1), the general formula (II-A), the general formula (II-B), the general formula (III-A), and the general formula (V) are contained at the same time,

in the formulae, R⁵ represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and R⁶ represents an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms.
 11. The liquid crystal composition according to claim 1, comprising a polymerizable compound.
 12. The liquid crystal composition according to claim 11, comprising, as the polymerizable compound, one or more compounds represented by general formula (IV),

in the formula, R⁷ and R⁸ each independently represent any of groups represented by formula (R-1) to formula (R-15) below,

and X¹ to X⁸ each independently represent a trifluoromethyl group, a trifluoromethoxy group, a fluorine atom, or a hydrogen atom.
 13. A liquid crystal display device using the liquid crystal composition according to claim
 1. 14. An active matrix driving liquid crystal display device using the liquid crystal composition according to claim
 1. 15. A liquid crystal display device for a VA mode, a PSA mode, a PSVA mode, an IPS mode, or an ECB mode, the liquid crystal display device using the liquid crystal composition according to claim
 1. 